4 The Bronze e Age Chalcolithic man was clearly aware of the many useful features of copper that made it preferable to stone or organic materials for some specialized applications.Among these properties were its elasticity and particularly plasticity,which allowed sheets or chunks of copper to be given useful shapes.Chalcolithic man also exploited the fact that copper hardens during hammering,that is,as a result of plastic deformation.Last but not least,molten copper can be cast into molds to obtain more intricate shapes. On the negative side,surface oxidation and gases trapped dur- ing melting and casting which may form porosity were probably of some concern to Chalcolithic man.More importantly,how- ever,cast copper is quite soft and thus could hardly be used for strong weapons or tools.Eventually,the time had come for a change through innovation.A new material had to be found.This material was bronze;see Fig.4.1. It is not known whether Chalcolithic man discovered by ex- perimentation or by chance that certain metallic additions to cop- per considerably improved the hardness of the cast alloy.(An al- loy is a combination of several metals.)In other words,cast bronze has a higher hardness than pure copper without necessi- tating subsequent hammering.Further,it had probably not es- caped the attention of Chalcolithic man that the melting tem- perature of certain copper alloys is remarkably reduced compared to pure copper (by about 100C as we know today) and that molten alloys flow more easily during casting. Naturally,some impurities that were already present in the copper ore transferred into the solidified copper.Among them were arsenic,antimony,silver,lead,iron,bismuth,and occa- sionally even tin.These impurities,however,were not present in sufficient quantities that one could refer to the resulting product as an alloy.Small quantities of these impurities rarely change
4 Chalcolithic man was clearly aware of the many useful features of copper that made it preferable to stone or organic materials for some specialized applications. Among these properties were its elasticity and particularly plasticity, which allowed sheets or chunks of copper to be given useful shapes. Chalcolithic man also exploited the fact that copper hardens during hammering, that is, as a result of plastic deformation. Last but not least, molten copper can be cast into molds to obtain more intricate shapes. On the negative side, surface oxidation and gases trapped during melting and casting which may form porosity were probably of some concern to Chalcolithic man. More importantly, however, cast copper is quite soft and thus could hardly be used for strong weapons or tools. Eventually, the time had come for a change through innovation. A new material had to be found. This material was bronze; see Fig. 4.1. It is not known whether Chalcolithic man discovered by experimentation or by chance that certain metallic additions to copper considerably improved the hardness of the cast alloy. (An alloy is a combination of several metals.) In other words, cast bronze has a higher hardness than pure copper without necessitating subsequent hammering. Further, it had probably not escaped the attention of Chalcolithic man that the melting temperature of certain copper alloys is remarkably reduced compared to pure copper (by about 100°C as we know today) and that molten alloys flow more easily during casting. Naturally, some impurities that were already present in the copper ore transferred into the solidified copper. Among them were arsenic, antimony, silver, lead, iron, bismuth, and occasionally even tin. These impurities, however, were not present in sufficient quantities that one could refer to the resulting product as an alloy. Small quantities of these impurities rarely change The Bronze Age
4·The Bronze Age 67 FIGURE 4.1.A portion of a mural from the tomb of the Vizier Rekh-Mi-Re at Thebes (Egypt) depicting workers carrying a piece of copper in the shape of an ox hide (see Figure 1.3)and baskets containing probably tin and lead for bronze production. An overseer "supervises"the porters.Second millenium B.c. (Reprinted by permission from B. Scheel,Egyptian Metalworking and Tools,Shire Publications, Aylesbury,UK) the properties of copper noticeably except in the case of bismuth, which even in small amounts makes copper brittle. The first major and deliberate addition to copper seemed to have been arsenic (at least in the Middle East).Copper-arsenic ores were widely available in this region,but alloying also was achieved by mixing arsenic-containing ores with copper ores during smelt- ing (see Plate 4.1).Artifacts from 3000 B.C.found in the Middle East contained up to 7%arsenic as a second constituent to cop- per.In this context,an archaeological find needs to be mentioned which was made in 1961.In the almost inaccessible "Cave of the Treasure,"close to the cave where the Dead Sea Scrolls were un- earthed,429 objects were discovered,of which all but 13 were made of a copper-arsenic alloy.They must have been brought there around 3000 B.C.by refugees and may have belonged to a temple or shrine.The cache harbored 10 crowns,240 elaborately deco- rated mace heads,chisels,and axes of different sizes and shapes. Copper-arsenic alloys,however,were used only for a limited time.Eventually,it must have been realized that the fumes which were emitted by the arsenic during smelting killed some metal- smiths.Eventually,tin was found to be the ideal addition to cop- per which was alloyed in an optimal proportion of 10 mass-%. This copper-tin alloy is generally referred to as bronze.The melt- ing temperature of Cu-10%Sn is about 950C (compared to 1084C for pure Cu).The melt flows freely into molds and no problems with gas bubbles,that is,porosity,are encountered. Most importantly,however,the alloy is hard immediately after casting and subsequent cooling but can be hardened further by hammering.Finally,copper-tin is harder and less brittle than copper-arsenic.See in this context Plate 4.2
the properties of copper noticeably except in the case of bismuth, which even in small amounts makes copper brittle. The first major and deliberate addition to copper seemed to have been arsenic (at least in the Middle East). Copper–arsenic ores were widely available in this region, but alloying also was achieved by mixing arsenic-containing ores with copper ores during smelting (see Plate 4.1). Artifacts from 3000 B.C. found in the Middle East contained up to 7% arsenic as a second constituent to copper. In this context, an archaeological find needs to be mentioned which was made in 1961. In the almost inaccessible “Cave of the Treasure,” close to the cave where the Dead Sea Scrolls were unearthed, 429 objects were discovered, of which all but 13 were made of a copper–arsenic alloy. They must have been brought there around 3000 B.C. by refugees and may have belonged to a temple or shrine. The cache harbored 10 crowns, 240 elaborately decorated mace heads, chisels, and axes of different sizes and shapes. Copper–arsenic alloys, however, were used only for a limited time. Eventually, it must have been realized that the fumes which were emitted by the arsenic during smelting killed some metalsmiths. Eventually, tin was found to be the ideal addition to copper which was alloyed in an optimal proportion of 10 mass–%. This copper-tin alloy is generally referred to as bronze. The melting temperature of Cu–10% Sn is about 950°C (compared to 1084°C for pure Cu). The melt flows freely into molds and no problems with gas bubbles, that is, porosity, are encountered. Most importantly, however, the alloy is hard immediately after casting and subsequent cooling but can be hardened further by hammering. Finally, copper–tin is harder and less brittle than copper–arsenic. See in this context Plate 4.2. 4 • The Bronze Age 67 FIGURE 4.1. A portion of a mural from the tomb of the Vizier Rekh-Mi-Re at Thebes (Egypt) depicting workers carrying a piece of copper in the shape of an ox hide (see Figure 1.3) and baskets containing probably tin and lead for bronze production. An overseer “supervises” the porters. Second millenium B.C. (Reprinted by permission from B. Scheel, Egyptian Metalworking and Tools, Shire Publications, Aylesbury, UK)
68 4·The Bronze Age There are several intriguing questions that demand answers. One of them is concerned with the query about whether or not bronze was "invented"in only one region of the world (namely the Middle East,as many scholars used to believe)or indepen- dently at several places.The final word on this has not been spo- ken yet.However,recent archaeological evidence indicates that besides the Mediterranean area(considered by many westerners to be the "cradle of civilization),independent bronze-producing centers existed in northern Thailand (Ban Chiang)during the third or fourth millennium B.c.,and additionally in the isolation of China during the Shang dynasty starting at about 1400 B.C. The mode of transition into the bronze age in the just- mentioned areas,which were considerably separated from each other,seemed not to have been identical.For example,Indo- China (which is said to have given to mankind a number of es- sential food plants such as rice,bananas,coconuts,yams,taro, and sugarcane)had a remarkable bronze production.The in- habitants of this area lived in light bamboo houses,made pot- tery,and domesticated pigs,chickens,and cows.In this region, bronze axes,spearheads,socket tools,bronze bracelets,clay cru- cibles,and sandstone molds have been found dating back as far as3000to2300B.c. The most interesting find is that the Ban Chiang people seemed to have skipped copper production and arsenical bronze alto- gether and jumped immediately into the tin-bronze age.The raw materials for bronze were certainly available at essentially one and the same place(in contrast to the Near East,as we shall elu- cidate below).Indeed,rich alluvial deposits of tin as well as cop- per ores are found from southern China down to Thailand and Indonesia.Another interesting observation was made by archae- ologists who state that the Thai people seemed to have lived in a "peaceful bronze age"since no swords,battle axes,daggers,or mace heads have been found.Instead,bronze was mostly used for decoration and adornment.Its possession did not seem to ex- press a status symbol since many children were buried with bronze bracelets. In contrast to this,early Chinese bronze,made during the Shang dynasty (1600-1122 B.c.),was mainly utilized for cere- monial vessels,that is,for offering of food and wine to ancestral spirits (Plate 4.3).The bronze contained from 5 to 30%tin and between 3 and 5%lead (which makes the melt flow easier). ISoil deposited by flowing water
There are several intriguing questions that demand answers. One of them is concerned with the query about whether or not bronze was “invented” in only one region of the world (namely the Middle East, as many scholars used to believe) or independently at several places. The final word on this has not been spoken yet. However, recent archaeological evidence indicates that besides the Mediterranean area (considered by many westerners to be the “cradle of civilization”), independent bronze-producing centers existed in northern Thailand (Ban Chiang) during the third or fourth millennium B.C., and additionally in the isolation of China during the Shang dynasty starting at about 1400 B.C. The mode of transition into the bronze age in the justmentioned areas, which were considerably separated from each other, seemed not to have been identical. For example, IndoChina (which is said to have given to mankind a number of essential food plants such as rice, bananas, coconuts, yams, taro, and sugarcane) had a remarkable bronze production. The inhabitants of this area lived in light bamboo houses, made pottery, and domesticated pigs, chickens, and cows. In this region, bronze axes, spearheads, socket tools, bronze bracelets, clay crucibles, and sandstone molds have been found dating back as far as 3000 to 2300 B.C. The most interesting find is that the Ban Chiang people seemed to have skipped copper production and arsenical bronze altogether and jumped immediately into the tin–bronze age. The raw materials for bronze were certainly available at essentially one and the same place (in contrast to the Near East, as we shall elucidate below). Indeed, rich alluvial1 deposits of tin as well as copper ores are found from southern China down to Thailand and Indonesia. Another interesting observation was made by archaeologists who state that the Thai people seemed to have lived in a “peaceful bronze age” since no swords, battle axes, daggers, or mace heads have been found. Instead, bronze was mostly used for decoration and adornment. Its possession did not seem to express a status symbol since many children were buried with bronze bracelets. In contrast to this, early Chinese bronze, made during the Shang dynasty (1600–1122 B.C.), was mainly utilized for ceremonial vessels, that is, for offering of food and wine to ancestral spirits (Plate 4.3). The bronze contained from 5 to 30% tin and between 3 and 5% lead (which makes the melt flow easier). 68 4 • The Bronze Age 1Soil deposited by flowing water
4·The Bronze Age 69 Bronze pieces from the Shang period are richly decorated by re- lief patterns depicting animals such as elephants,water buffalos, tigers,mythical dragons,and others.The Chinese were masters of a cast technology (Plate 4.3).They utilized fired clay molds in which the patterns were carved.No subsequent metalworking such as hammering,etc.,was used.An example of their skills is a large cauldron on four legs which weighs 875 kg and whose body was cast in one piece.(It was unearthed near Anyang in 1939 and then utilized by villagers for storing pig food.) Another astounding recent find is a set of bronze bells which were discovered in a tomb for the Marqui Yi,dated 433 B.C.(Fig. 4.2).They were shaped in a manner that,when hit with a ham- mer at the center,produced a lower pitch than on the edge.Mod- ern scholars believe that the two sounds reflected the Chinese concept of a universe that is governed by two opposing,yet har- monious,forces called Yin and Yang (such as day and night, heaven and earth,sun and moon).The two-tone bells are said to have demonstrated how two forces can interact in harmony.Mu- FIGURE 4.2.Chinese two-tone bell made of bronze.Eastern Zhou dy- nasty,6th century B.C.Unearthed in 1978 at Sui Xian,Hubei Province.An entire set of those bells is called“Bian Zhong”. Arthur M.Sackler Gallery,Smith- sonian Institution,Washington, DC.Gift of Arthur M.Sackler S1987.285
Bronze pieces from the Shang period are richly decorated by relief patterns depicting animals such as elephants, water buffalos, tigers, mythical dragons, and others. The Chinese were masters of a cast technology (Plate 4.3). They utilized fired clay molds in which the patterns were carved. No subsequent metalworking such as hammering, etc., was used. An example of their skills is a large cauldron on four legs which weighs 875 kg and whose body was cast in one piece. (It was unearthed near Anyang in 1939 and then utilized by villagers for storing pig food.) Another astounding recent find is a set of bronze bells which were discovered in a tomb for the Marqui Yi, dated 433 B.C. (Fig. 4.2). They were shaped in a manner that, when hit with a hammer at the center, produced a lower pitch than on the edge. Modern scholars believe that the two sounds reflected the Chinese concept of a universe that is governed by two opposing, yet harmonious, forces called Yin and Yang (such as day and night, heaven and earth, sun and moon). The two-tone bells are said to have demonstrated how two forces can interact in harmony. Mu- 4 • The Bronze Age 69 FIGURE 4.2. Chinese two-tone bell made of bronze. Eastern Zhou dynasty, 6th century B.C. Unearthed in 1978 at Sui Xian, Hubei Province. An entire set of those bells is called “Bian Zhong”. Arthur M. Sackler Gallery, Smithsonian Institution, Washington, DC. Gift of Arthur M. Sackler S1987.285
704·The Bronze Age sic,which was important to the Chinese of that time,was a means to communicate with their forefathers,who gave them life and wealth.Music from bells and drums was not a form of enter- tainment but a ceremonial feast for and with their ancestors.It is still a mystery how the Chinese of the fifth century B.C.were able to cast two-tone bells.The bronze bells of the Marqui Yi weigh about 2500 kg,they are nicely decorated,and must have represented a large portion,if not all,of the wealth of their owner. It is believed today that China developed its bronze technology only slightly later than the West and independently from the out- side world.It grew,as in the West,out of the ceramic tradition. Chinese potters achieved kiln temperatures as high as 1400C which allowed them to produce their unique porcelain.In con- trast to Thailand,China briefly went through an initial copper smelting period (at around 2000 B.C.).But arsenic-bronzes seem to be absent in China.Furthermore,two types of bronzes were developed,one consisting of the usual copper-tin alloy and the other of copper with lead.Also interesting is a find of a piece of brass(copper-zinc),dating back to about 2200-2000 B.C.,which was probably smelted from zinc-bearing copper ore. As outlined above,both the Chinese and the Thais possessed ample copper as well as tin raw materials.This was definitely not true for the Chalcolithic man residing in the Near East.Ma- jor bronze-producing centers in 2000 B.C.were in Mesopotamia,! Assyria,Anatolia,and Cyprus.2.3 All of these centers were blessed with abundant deposits of copper ore,as described in Chapter 1. However,no tin seemed to have been found in the vicinity of these places.As a matter of fact,the major tin deposits as known today are in China,Thailand,Malaysia,England,Germany,Nige- ria,Zaire,Australia,Bolivia,and Mexico.They consist of tin ox- ide,or cassiterite (see Plate 4.1),which is inserted into granite in the form of veins.Cassiterite4 is broken down by water and washed into rivers where it can be panned like gold.Minor de- posits were possibly in Italy,Spain,France(at the mouth of the river Loire)and Sardinia. In short,reputed archaeological evidence seems to point to the fact that,during the Chalcolithic time,no major known tin sources were situated in the Near East except possibly for some Mesopotamia once lay between the lower Tigris and lower Euphrates rivers and is today part of Iraq.(From Greek:mesos middle and po- tomos river. 2Kypros (Greek)=copper. 3Aes cyprium (Latin)=copper;aes (Latin)=ore. Kassiteros (Greek)=tin
sic, which was important to the Chinese of that time, was a means to communicate with their forefathers, who gave them life and wealth. Music from bells and drums was not a form of entertainment but a ceremonial feast for and with their ancestors. It is still a mystery how the Chinese of the fifth century B.C. were able to cast two-tone bells. The bronze bells of the Marqui Yi weigh about 2500 kg, they are nicely decorated, and must have represented a large portion, if not all, of the wealth of their owner. It is believed today that China developed its bronze technology only slightly later than the West and independently from the outside world. It grew, as in the West, out of the ceramic tradition. Chinese potters achieved kiln temperatures as high as 1400°C which allowed them to produce their unique porcelain. In contrast to Thailand, China briefly went through an initial copper smelting period (at around 2000 B.C.). But arsenic–bronzes seem to be absent in China. Furthermore, two types of bronzes were developed, one consisting of the usual copper–tin alloy and the other of copper with lead. Also interesting is a find of a piece of brass (copper–zinc), dating back to about 2200–2000 B.C., which was probably smelted from zinc-bearing copper ore. As outlined above, both the Chinese and the Thais possessed ample copper as well as tin raw materials. This was definitely not true for the Chalcolithic man residing in the Near East. Major bronze-producing centers in 2000 B.C. were in Mesopotamia,1 Assyria, Anatolia, and Cyprus.2,3 All of these centers were blessed with abundant deposits of copper ore, as described in Chapter 1. However, no tin seemed to have been found in the vicinity of these places. As a matter of fact, the major tin deposits as known today are in China, Thailand, Malaysia, England, Germany, Nigeria, Zaire, Australia, Bolivia, and Mexico. They consist of tin oxide, or cassiterite (see Plate 4.1), which is inserted into granite in the form of veins. Cassiterite4 is broken down by water and washed into rivers where it can be panned like gold. Minor deposits were possibly in Italy, Spain, France (at the mouth of the river Loire) and Sardinia. In short, reputed archaeological evidence seems to point to the fact that, during the Chalcolithic time, no major known tin sources were situated in the Near East except possibly for some 70 4 • The Bronze Age 1Mesopotamia once lay between the lower Tigris and lower Euphrates rivers and is today part of Iraq. (From Greek: mesos middle and potomos river.) 2Kypros (Greek) copper. 3Aes cyprium (Latin) copper; aes (Latin) ore. 4Kassiteros (Greek) tin